Ranger PBT PBT-201-G20 202
Polybutylene Terephthalate
Beijing Ranger Chemical Co., Ltd.
产品说明：
Unreinforced grades have abundant strength andflexibility, and have strong characteristics againstbrittleness.
UL-certified slow-burning(94HB) and self-extinguishinggrades(94V-0,V-2) exist, and electrical properties exhibited arethe highest of any thermoplastic.
Low water absorption is exhibited, and excellent electricalproperties(CTI and GWIT) are retained over extended periods ofusages, even with widely varied temperature and humidityconditions.
The surface of molded products is smooth, and a low coefficient offriction is exhibited.As the amount of froction is low, PBT issuitable for use in application requiring friction and wearproperties.
The material is exceptionally reliable, with small in-usedimensional variation, and superior molding stability anddimensional precision.
Long-term chemical resistance is exceptional, and at roomtemperature, there is almost no degradation in propertiesafter.
Both unreinforced and reinforced grades exhibit exceptionalflowability, and excellent processability.
Application:VCD drive frames\ Connectors\ Trimmers\ Switch buttonsfor gas-fired instantaneous water heaters\ Relay blocks\ Driers\Rectifiers\ Outer handles\ Height sensor cases\ Door mirror stays\Drive component housings\ Energy saving lamp.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.54 | g/cm³ | ASTM D792 |
| 收缩率 - 流动 | 0.40 到 1.1 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (屈服) | 105 | MPa | ASTM D638 |
| 弯曲模量 | 7000 | MPa | ASTM D790 |
| 弯曲强度 | 160 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 8.0 | kJ/m² | ASTM D256 |
| 无缺口伊佐德冲击强度 | 50 | kJ/m² | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 212 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 203 | °C | ASTM D648 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 (2.00 mm) | 1.2E+16 | ohms·cm | ASTM D257 |
| 介电强度 (2.00 mm) | 20 | kV/mm | ASTM D149 |
| 介电常数 (50 Hz) | 3.20 | ASTM D150 | |
| 耗散因数 (50 Hz) | 0.020 | ASTM D150 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒后部温度 | 225 到 250 | °C | |
| 料筒中部温度 | 225 到 250 | °C | |
| 料筒前部温度 | 225 到 250 | °C | |
| 射嘴温度 | 240 | °C | |
| 模具温度 | 60.0 到 80.0 | °C | |
| 注塑压力 | 60.0 到 120 | MPa | |
| 背压 | 6.00 到 18.0 | MPa | |
| 螺杆转速 | < 100 | rpm |
| 注射说明 |
|---|
| Injection Time: 3 to 15 secTime Pressure: 2 to 5 secTotalCycle: 15 to 50 sec |